Research Article
Snehasis Jana, Omprakash L,
Abstract
Bronze, a copper-tin alloy, widely utilizing in manufacturing of gears, bearing, and packing technologies due to its versatile physical, mechanical, and chemical properties. The aim of the present work was to evaluate the effect of bio-field treatment on physical and structural properties of bronze powder. Bronze powder was divided into two samples, one served as control and the other sample was received bio-field treatment. Control and treated bronze samples were characterized using x-ray diffraction (XRD), particle size analyzer, scanning electron microscopy (SEM), and Fourier transform infrared (FT-IR) spectroscopy. XRD result showed that the unit cell volume was reduced upto 0.78% on day 78 in treated bronze as compared to control. Further, the crystallite size was significantly reduced upto 49.96% in treated bronze sample on day 106 as compared to control. In addition, the bio-field treatment has significantly reduced the average particle size upto 18.22% in treated bronze powder as compared to control. SEM data showed agglomerated and welded particles in control bronze powder, whereas fractured morphology at satellites boundaries were observed in treated bronze. The yield strength of bronze powder calculated using Hall- Petch equation, was significantly changed after bio-field treatment. The FT-IR analysis showed that there were three new peaks at 464 cm-1, 736 cm-1, and 835 cm-1 observed in treated bronze as compared to control; indicated that the bio-field treatment may alter the bond properties in bronze. Therefore, the bio-field treatment has substantially altered the characteristics of bronze at physical and structural level.