Abstract
It is known that in traditional power engineering hydrogen may be one of the firstprimary source of equipment damage [1]. This problem has high actuality for both nuclear and thermonuclear power engineering [2]. Particularly reactor pressure vessels (RPV) of the WWER-440/230 project were manufactured without stainless cladding that were in contact with primary circuit water and accessible for hydrogen as a product of RPV wall corrosion. Analysis of the combined radiation-hydrogenation embrittlement of the 48TS type vessel steel was performed in [3] where at the mention of the American [4] and own data question concerning unknown source of hydrogen in metal that was irradiated in nuclear reactor in hermetic ampoules (was named as “irradiation-produced hydrogen” (IPH) was raised.